Photoconductor including hydrazone compound in a photoconductive layer

ABSTRACT

A photoconductor for electrophotography comprising a novel hydrazone compound or derivative as a charge transporting substance. A hydrazone compound is represented by the following general formula: ##STR1## wherein, each of R 1 , R 2 , R 3 , R 4 , R 5  and R 6  stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, a nitro group, an allyl group, or an aryl group which may have a substituent(s) or an amino group which may have a substitutent(s); and n stands for an integer of 0, 1 or 2.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a photoconductor for electrophotography, and particularly to a photoconductor for electrophotography which contains a novel hydrazone compound in the photosensitive layer thereof formed on an electroconductive substrate.

2. Description of the Prior Art

Photosensitive materials which have heretofore been used in photoconductors for electrophotography include inorganic photoconductive substances such as selenium and selenium alloys, dispersions of inorganic photoconductive substances such as zinc oxide and cadmium sulfide in resin binders, organic polymeric photoconductive substances such as poly-N-vinylcarbazole and polyvinylanthracene, organic photoconductive substances such as phthalocyanine compounds and bisazo compounds, and dispersions of such organic polymeric photoconductive substances in resin binders.

Photoconductors are required to have the capability of maintaining a surface electric charge in the dark, of generating an electric charge upon receiving light, and of transporting an electric charge upon receiving light. They are classified into two types of photoconductors, namely so-called monolayer type photoconductors, and so-called laminate type photoconductors. The former comprises a single layer having all of the above-mentioned characteristics, and the latter comprises functionally distinguishable laminated layers, one of which contributes mainly to the generation of electric charge, and another of which contributes to the retention of surface electric charge in the dark and the transportation of electric charge upon receiving light. An example of an electrophotographic method using a photoconductor of the kind mentioned above, is the Carlson's system applied to image formation. Image formation according to this system comprise the steps of subjecting a photoconductor kept in the dark to corona discharge to charge the photoconductor, illuminating the surface of the charged photoconductor with imagewise light derived from a manuscript or copy bearing, e.g., letters and/or pictures to form a latent electrostatic image, developing the formed latent electrostatic image with a toner, and transferring the developed toner image to a support such as a paper sheet to fix the toner image on the support. After the toner image transfer, the photconductor is subjected to the steps of removal of the electric charge, removal of the remaining toner (cleaning), neutralization of the residual charge with light (erasure), and so on to be ready for reuse.

Photosensitive members for electrophotography in which use is made of at least one organic material have recently been put into practical use by virtue of the advantageous features of organic materials such as flexibility, thermal stability, and/or a film forming capacity. They include a photoconductor comprising poly-N-vinylcarbazole and 2,4,7-trinitrofluoren-9-one (disclosed in U.S. Pat. No. 3,484,237), a photoconductor using an organic pigment as the main component (disclosed in Japanese Patent Laid-Open No. 37,543/1972), and a photoconductor using as a main component a eutectic complex composed of a dye and a resin (disclosed in Japanese Patent Laid-Open No. 10,785/1972). A number of novel hydrazone compounds have also been put into practical use as photoconductors.

Although organic materials have a number of the advantageous features mentioned above with which inorganic materials are not endowed, the fact is that there have been obtained no organic materials fully satisfying all the characteristics required of a material to be used in photoconductors for electrophotography. Particular problems involved in the use of organic materials have been photosensitivity and repeatability in continuous use.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a photoconductor for electrophotography to be used in copying apparatuses and printers which photoconductor has a high photosensitivity and excellent characteristics in repeated use, through the use, in the photosensitive layer, of a novel organic materials as a charge transporting substance.

In one embodiment of the present invention, a photoconductor for electrophotography comprises:

at least one hydrazone compound represented by the following general formula (I) as a charge transporting substance: ##STR2## wherein each of R₁, R₂, R₃, R₄, R₅ and R₆ stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, a nitro group, an allyl group, or an aryl group or an amino group both of which may have at least one substituent; and n stands for an integer of 0, 1 or 2.

Here, the photoconductor may comprise a single layer including a dispersion of a charge generating substance and a charge transporting substance selected from hydrazone compounds represented by the general formulae (I) in a binder resin.

Alternatively the photoconductor may comprise a laminate of a charge transporting layer, including a charge transporting substance selected from hydrazone compounds represented by the general formulae (I), and a charge generating layer.

In the another embodiment of the present invention, a photoconductor for electrophotography comprises:

at least one hydrazone compound represented by the following general formula (II) as a charge transporting substance: ##STR3## wherein each of R₇, R₈, R₉, R₁₀ and R₁₁ stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, an acyl group, a nitro group, or an aryl group or an amino group, both of which may have at least one substituent, m stands for an integer 2, 3, 4 or 5; and n stands for an integer of 0, 1 or 2.

Here, the photoconductor may comprise a single layer including a dispersion of a charge generating substance and a charge transporting substance selected from hydrazone compounds represented by the general formulae (II) in a binder resin.

Alternatively, the photoconductor may comprise a laminate of a charge transporting layer, including a charge transporting substance selected from hydrazone compounds represented by the general formulae (II) and a charge generating layer.

The above and other objects, effects, features and attendant advantages of the present invention will become more apparent from the following description of embodiments thereof taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 to 3 are schematic cross-sectional views of photoconductors according to the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

A photoconductor according to the present invention which contains a hydrazone compound in the photosensitive layer may be in the form of any one of the structures of FIGS. 1, 2 and 3, depending on the kind of application of the hydrazone compound thereto.

FIGS. 1, 2 and 3 are schematic cross-sectional views of different embodiments of the photoconductor of the present invention, respectively.

FIG. 1 shows a monolayer-type photoconductor. A photosensitive layer 2A is provided on an electroconductive substrate 1. The photosensitive layer 2A comprises a charge generating substance 3 and a hydrazone compound as a charge transporting substance 5 both of which are dispersed in a resin binder matrix so that the photosensitive layer 2A functions as a photoconductor.

FIG. 2 shows a laminate-type photoconductor. A laminated photosensitive layer 2B is provided on an electroconductive substrate 1. A lower layer of the laminate is a charge generating layer 4 including a charge generating substance 3 as the main component and an upper layer is a charge transporting layer 6 containing a hydrazone compound as a charge transporting substance 5. Accordingly, the photosensitive layer 2B functions as a photoconductor. This photoconductor is usually used in the negative charge mode.

FIG. 3 shows another laminate-type photoconductor having a layer structure in reverse to that of FIG. 2. A laminated photosensitive layer 2C is provided on an electroconductive substrate 1. The lower layer of the laminate is a charge transporting layer 6 including a hydrazone compound as a charge transporting substance 5 and an upper one is a charge generating layer 4 including a charge generating substance 3. The photosensitive layer also functions as a photoconductor. This photoconductor is usually used in the positive charge mode. In this case, a covering layer 7 may generally be further provided as shown in FIG. 3 to protect the charge generating layer 4.

Thus, there are two different types of layer structures in the photoconductor. The reason for this is that, even if a photoconductor with the layer structure as shown in FIG. 2 is to be used in the positive charge mode, no charge transporting substances adaptable to the positive charge mode have been found yet. Accordingly, when the positive charge mode is to be used the photoconductor of the layer structure as shown in FIG. 3 is presently required.

A photoconductor as shown in FIG. 1 can be produced by dispersing a charge generating substance in a solution of a charge transporting substance and a resin binder and applying the resulting dispersion on an electroconductive substrate.

A photoconductor as shown in FIG. 2 can be prepared by depositing a charge generating substance on an electroconductive substrate by means of vacuum evaporation or applying and drying a dispersion of a particulate charge generating substance in a solvent and/or a resin binder on an electroconductive substrate, followed by applying a solution of a charge transporting substance and a resin binder on the charge-generating layer and drying.

A photoconductor as shown in FIG. 3 can be prepared by applying and drying a solution of a charge transporting substance and a resin binder on an electroconductive substrate, and depositing a charge generating substance on the resulting charge-generating layer by means of vacuum evaporation or by coating and drying a dispersion of a particulate charge generating substance in a solvent and/or a resin binder on the charge-generating followed by formation of a covering layer.

The electroconductive substrate 1 serves as an electrode for the photoconductor and as a support for a layer(s) formed thereon. The electroconductive substrate may be in the form of a cylinder, a plate or a film, and may be made of a metallic material such as aluminum, stainless steel or nickel, or other material having a surface treated to be electroconductive, such as glass so treated or a resin so treated.

The charge generating layer 4 is formed by application of a dispersion of a particulate charge generating substance 3 in a resin binder or by deposition of a charge generating substance by means of vacuum evaporation, or the like technique as described above, and this layer generates an electric charge upon receiving light. It is important that the charge generating layer 4 be high not only in charge generating efficiency but also in capability of injecting the generated electric charge into the charge transporting layer 6 and any covering layer 7. This capability is desirably as little dependent upon any electric field as possible and is high even in low intensity electric fields. Usable charge generating substances include phthalocyanine compounds such as metal-free phthalocyanine and titanyl phthalocyanine; various azo, quinone and indigo pigments; dyes such as cyanine, squarylium, azulenium, and pyrylium compounds; and selenium and selenium compounds. Among these, a suitable compound can be chosen depending on the wavelength range of a light source used for the image formation. The thickness of the charge generating layer is determined depending on the extinction coefficient of the charge generating substance to be used therein in view of the layer's function of generating an electric charge, but is generally 5 μm or less, and preferably 1 μm or less. It also is possible to form a charge generating layer using a charge generating substance as the main component in a mixture with a charge transporting substance and so on. Resin binders usable in the charge generating layer include polycarbonates, polyesters, polyamides, polyurethanes, epoxy resins, silicone resins, and methacrylate homopolymer and copolymers, which may be used either alone or in an appropriate composition ratio.

The charge transporting layer 6 is a coating film containing a hydrazone compound as an organic charge transporting substance in a resin binder. The charge transporting layer serves as an insulator layer in the dark so as to retain the electric charge of the photoconductor, and fulfills the function of transporting an electric charge injected from the charge generating layer upon receiving light. Resin binders usable in the charge transporting layer include polycarbonates, polyesters, polyamides, polyurethanes, epoxy resins, silicone resins, and methacryate homopolymer and copolymers.

The covering layer 7 has the function of receiving and retaining an electric charge generated by corona discharge in the dark and the capability of transmitting light to which the charge generating layer should respond. It is necessary that the covering layer transmits light upon exposure of the photoconductor and allows the light to reach the charge generating layer, and then receives the injection of the electric charge generated in the charge generating layer to neutralize and erase the surface electric charge. Materials usable in the covering layer include organic insulating film-forming materials such as polyesters and polyamides. Such organic materials may also be used in mixture with an inorganic material such as a glass resin or SiO₂, or a material for lowering electric resistance such as a metal or a metallic oxide. Materials usable in the covering layer are not limited to organic insulating materials for film-forming, and further include inorganic materials such as SiO₂, metals, and metallic oxides, which may be formed into a covering layer by appropriate methods such as vacuum evaporation and deposition, or sputtering. From the viewpoint of the aforementioned description, it is desirable that the material to be used in the covering layer be as transparent as possible in the wavelength range in which the charge generating substance attains maximum light absorption.

Although the thickness of the covering layer depends on the material or composition thereof, it can be arbitrarily set in so far as it does not produce any adverse effects including an increase in a residual potential in continuous repeated use.

The hydrazone compounds to be used in the present invention can be easily synthesized by known methods.

The first group of hydrazone compounds is represented by the following general formula (I). ##STR4## Wherein, each of R₁, R₂, R₃, R₄, R₅ and R₆ stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, a nitro group, an allyl group, or an aryl group or an amino group both of which may have a substituent(s); and n stands for an integer of 0, 1 or 2.

These compounds are synthesized by the dehydration-condensation reaction of an aldehyde compound of the formula ##STR5## with a hydrazine compound of the formula ##STR6## in an appropriate organic solvent such as ethanol in the presence of a small amount of a catalyst such as an acid.

Specific examples of the hydrazone compounds of the general formula (I) prepared in the above-mentioned manner include: ##STR7##

Examples will now be given, wherein various compounds represented by the general formula (I) were respectively used to produce photoconductors.

EXAMPLE I-1

50 parts by weight of metal-free phthalocyanine (manufactured by Tokyo Kasei CO., Ltd.) were pulverized with a ball mill for 150 hours and 100 parts by weight of the hydrazone compound No. I-1 mentioned above were kneaded together with 100 parts by weight of a polyester resin (Vylon 200 (trademark), manufactured by Toyobo Co., Ltd.) and tetrahydrofuran (THF) as a solvent with a mixer for 3 hours to prepare a coating liquid. The coating liquid was applied on an aluminum-deposited polyester film (Al-PET) as an electroconductive substrate by means of the wire bar technique to form a photosensitive layer having a dry thickness of 15 μm. Thus, a photoconductor with the structure shown in FIG. 1 was produced.

EXAMPLE I-2

Metal-free α-phthalocyanine as a starting material was pulverized for 20 minutes into a fine powder with a pulverizer, a LIMMAC (Linear Induction Motor Mixing and Crushing manufactured by Fuji Electric Co., Ltd.), wherein a non-magnetic can containing the metal-free α-phthalocyanine and Teflon pieces as small acting pieces was placed between two linear motors faced each other. A sample of 1 part by weight of the fine powder thus prepared was dispersed in 50 parts by weight of DMF (N,N-dimethylformamide) as a solvent by means of ultrasonic dispersion treatment. Thereafter, the sample was separated from DMF by filtration and dried to complete the treatment of metal-free phthalocyanine.

A solution of 100 parts by weight of the hydrazone compound No. I-2 mentioned above in 700 parts by weight of tetrahydrofuran (THF) was mixed with a solution of 100 parts by weight of polymethyl methacrylate (PMMA, manufactured by Tokyo Kasei Co., Ltd.) in 700 parts by weight of toluene to prepare a coating liquid. The coating liquid was applied on an aluminum-deposited polyester film substrate by means of the wire bar technique to form a charge transporting layer having a dry thickness of 15 μm. 50 parts by weight of metal-free phthalocyanine treated in the above-mentioned manner, 50 parts by weight of a polyester resin (Vylon 200), and 50 parts by weight of PMMA were kneaded with a mixer for 3 hours together with THF as a solvent to prepare a coating liquid, which was then applied on the charge transporting layer by the wire bar technique to form a charge generating layer having a dry thickness of 1 μm. Thus, a photoconductor with a structure corresponding to that shown in FIG. 3 was produced.

EXAMPLE I-3

A photoconductor was produced by forming a photosensitive layer in substantially the same manner as in example I-1 except that 50 parts by weight of metal-free phthalocyanine, 100 parts by weight of the hydrazone compound No. I-3 mentioned above, 50 parts by weight of a polyester resin (Vylon 200), and 50 parts by weight of PMMA were used to replace therewith the composition of the photosensitive layer of Example I-1.

EXAMPLE I-4

A photoconductor was produced by forming a photosensitive layer in substantially the same manner as in Example I-1 except that Chlorodiane Blue which is a bisazo pigment disclosed in, for example, Japanese Patent Laid-Open No. 37,543/1972 was used instead of metal-free phthalocyanine in the Example I-3.

The electrophotographic characteristics of the four photoconductors thus produced were measured by utilizing an electrostatic recording paper testing apparatus (Kawaguchi Denki Model SP-428).

The surface potential V_(s) (volts) of each photoconductor is an initial surface potential which was measured when the surface of the photoconductor was positively charged in the dark by corona discharge at +6.0 kV for 10 seconds. After the discontinuation of the corona discharge, the photoconductor was allowed to stand in the dark for 2 seconds, after which the surface potential V_(d) (volts) of the photoconductor was measured. Subsequently, the surface of the photoconductor was irradiated with white light at an illuminance of 2 luxes and the time (seconds) required for the irradiation to decrease the surface potential of the photoconductor to half of V_(d) was measured. From that time and the illuminance the half decay exposure amount E_(1/2) (lux·sec) was calculated. Also, the surface potential of the photoconductor after 10 seconds of irradiation thereof with white light at an illuminance of 2 luxes was measured as the residual potential V_(r) (volts). When a phthalocyanine compound was used as a charge generating substance, a high sensitivity could be expected for light with longer wavelengths. Hence, the electrophotographic characteristics thereof were also measured by using monochromatic light with a wavelength of 780 nm. Specifically, the V_(s) and the V_(d) of each photoconductor were measured in the same manner as described above, and the half decay exposure amount (μJ/cm²) was found by irradiation of the photoconductor surface with a monochromatic light (wavelength: 780 nm) of 1 μW instead of white light, while the residual potential V_(r) (volts) was measured after 10 seconds of irradiation of the photoconductor surface with the above-mentioned light. The results of the measurements are shown in Table 1.

                  TABLE 1                                                          ______________________________________                                                              Light with Wavelength                                     White Light          of 780 nm                                                                           E.sub.1/2        E.sub.1/2                           Example V.sub.s V.sub.r   (lux ·                                                                     V.sub.s                                                                              V.sub.r                                                                              (μJ/                             No.     (volts) (volts)   sec) (volts)                                                                              (volts)                                                                              cm.sup.2)                           ______________________________________                                         I-1     600     90        5.4  630   80    5.2                                 I-2     640     110       6.2  610   90    5.1                                 I-3     670     80        6.8  610   70    6.0                                 I-4     660     30        5.6  --    --    --                                  ______________________________________                                    

As can be seen in Table 1, the photoconductors of Examples I-1, I-2, I-3 and I-4 were not substantially different in the half decay exposure amounts and the residual potentials, and showed good surface potential characteristics. The photoconductors of Examples I-1, I-2 and I-3, using a phthalocyanine compound as the charge generating substance, showed also excellent electrophotographic characteristics for light with of the long wavelength of 780 nm, proving that they can be satisfactorily used in semiconductor laser printers.

EXAMPLE I-5

Selenium was deposited on an aluminum plate having a thickness of 500 μm by means of vacuum evaporation to form a charge generating layer having a thickness of 1.5 μm. A solution of 100 parts by weight of the hydrazone compound No. I-4 as mentioned above in 700 parts by weight of tetrahydrofuran (THF) was mixed with a solution of 100 parts by weight of polymethyl methacrylate (PMMA) in 700 parts by weight of toluene to prepare a coating liquid, which was then applied on the charge generating layer by the wire bar techniue to form a charge transporting layer having a dry thickness of 20 μm. Thus, a photoconductor with the structure shown in FIG. 2 was produced. This photoconductor was charged by corona discharge at -6.0 kV for 0.2 second and good electrophotographic characteristics were obtained, namely V_(s) =-620 V, V_(r) =-40 V and E_(1/2) =4.8 lux·sec.

EXAMPLE I-6

50 parts by weight of metal-free phthalocyanine treated in the same manner as in Example I-1, 50 parts by weight of a polyester resin (Vylon 200), and 50 parts by weight of PMMA were kneaded together with THF as a solvent with a mixer for 3 hours to prepare a coating liquid, which was then applied on an aluminum support to form a charge generating layer having a thickness of about 1 μm. Subsequently, 100 parts by weight of the hydrazone compound No. I-5 as mentioned above, 100 parts by weight of a polycarbonate resin (Panlite L-1250, manufactured by Teijin Kasei Co., Ltd.), and 0.1 part by weight of a silicone oil were mixed with 700 parts by weight of THF and 700 parts by weight of toluene to prepare a coating liquid, which was then applied on the charge generating layer to form a charge transporting layer having a thickness of about 15 μm.

The photoconductor thus produced was charged by corona discharge at -6.0 kV for 0.2 second and examined with respect to electrophotographic characteristics in the same manner as in Example I-5, obtaining good results, namely V_(s) =-660 V and E_(1/2) =5.9 lux·sec.

EXAMPLE I-7

Photosensitive members were produced by forming respective photosensitive layers in substantially the same manner as in Example I-4 except that the compounds Nos. I-6 to I-21 were respectively used instead of the compound No. I-4. The results obtained by using the electrostatic recording paper testing apparatus (SP-428) are shown in Table 2. Table 2 shows the half decay exposure amounts E_(1/2) (lux·sec) obtained under the experimental conditions where the photoconductors were positively charged in the dark by corona discharge at +6.0 kV for 10 seconds and irradiated with white light at an illuminance of 2 luxes.

                  TABLE 2                                                          ______________________________________                                                         E.sub.1/2                                                      Compound No.    (lux · sec)                                           ______________________________________                                         I-6             7.1                                                            I-7             5.9                                                            I-8             6.4                                                            I-9             6.8                                                            I-10            6.5                                                            I-11            5.4                                                            I-12            6.8                                                            I-13            5.7                                                            I-14            5.2                                                            I-15            7.5                                                            I-16            5.8                                                            I-17            5.4                                                            I-18            5.9                                                            I-19            8.3                                                            I-20            6.5                                                            I-21            7.9                                                            ______________________________________                                    

As can be seen in Table 2, the photoconductors using the respective hydrazone compounds Nos. I-6 to I-21 as a charge transporting substance were satisfactory with respect to the half decay exposure amount E_(1/2).

The second group of hydrazone compounds to be used in the present invention is represented by the following general formula (II): ##STR8## wherein, each of R₇, R₈, R₉, R₁₀ and R₁₁ stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, an acyl group, a nitro group, an aryl group which may have a substituent(s), or an amino group which may have a substituent(s); and m stands for an integer of 2, 3, 4 or 5; and n stands for an integer of 0, 1 or 2.

These compounds are synthesized by the dehydration-condensation reaction of an aldehyde compound of the formula ##STR9## with a hydrazine compound of the formula ##STR10## in an appropriate organic solvent such as ethanol in the presence of a small amount of a catalyst such as an acid.

Specific examples of hydrazone compounds of the general formula (II) prepared in the above-mentioned manner include: ##STR11##

Examples will now be given, wherein various compounds represented by the general formula (II) were respectively used to produce photoconductors.

EXAMPLE II-1

A photoconductor having the structure shown in FIG. 1 and comprising a photosensitive layer having a thickness of 15 μm was produced in substantially the same manner as in Example I-1 except that the hydrazone compound No. II-1 mentioned above was used instead of the compound No. I-1.

EXAMPLE II-2

A photoconductor having a structure corresponding to that of FIG. 3 was produced in substantially the same manner as in Example I-2 except that the hydrazone compound No. II-2 was used instead of the compound No. I-2. The thickness of the charge transporting layer of the member was 15 μm, while the thickness of the charge generating layer was 1 μm.

EXAMPLE II-3

A photoconductor was produced by forming a photosensitive layer in substantially the same manner as in Example II-1 except that 50 parts by weight of metal-free phthalocyanine, 100 parts by weight of the hydrazone compound No. II-1 mentioned above, 50 parts by weight of a polyester resin (Vylon 200), and 50 parts by weight of PMMA were used to replace therewith the composition of the photosensitive layer of Example II-1.

EXAMPLE II-4

A photoconductor was produced by forming a photosensitive layer in substantially the same manner as in Example II-1 except that Chlorodiane Blue was used instead of metal-free phthalocyanine in the Example II-3.

The four photoconductors thus produced were examined with respect to surface potential V_(s), residual potential V_(r), and half decay exposure amount E_(1/2) by using white light as well as a monochromatic light (wavelength: 780 nm) in the same manner as in Examples I-1 to I-4. The results of the measurements are shown in Table 3.

                  TABLE 3                                                          ______________________________________                                                              Light with Wavelength                                     White Light          of 780 nm                                                                           E.sub.1/2        E.sub.1/2                           Example V.sub.s V.sub.r   (lux ·                                                                     V.sub.s                                                                              V.sub.r                                                                              (μJ/                             No.     (volts) (volts)   sec) (volts)                                                                              (volts)                                                                              cm.sup.2)                           ______________________________________                                         II-1    600     80        6.0  630   90    6.2                                 II-2    640     40        4.9  630   70    5.4                                 II-3    630     50        6.3  660   70    5.6                                 II-4    660     40        5.8  --    --    --                                  ______________________________________                                    

As can be seen in Table 3, the photoconductors of Examples II-1, II-2, II-3 and II-4 were not substantially different therebetween in the half decay exposure amount and the residual potential, and showed good surface potential characteristics. The photoconductors of Examples II-1, II-2 and II-3, using a phthalocyanine compound as a charge generating substance, also showed excellent electrophotographic characteristics for light with the long wavelength of 780 nm, and proving that they can be satisfactorily used in semiconductor laser printers.

EXAMPLE II-5

A photoconductor with the structure shown in FIG. 2 was produced by forming a charge generating layer and a charge transporting layer having a dry thickness of 20 μm in the same manner as in Example I-5 except that the hydrazone compound NO. II-4 was used instead of the compound No. I-4. After this photoconductor was charged by corona discharge at -6.0 kV for 0.2 second, the electrophotographic characteristics of the sample were measured, obtaining good results, namely V_(s) =-600 V, V_(r) =-40 V, and E_(1/2) =5.0 lux·sec.

EXAMPLE II-6

A charge generating layer with a thickness of about 1 μm was formed on an aluminum support in the same manner as in Example I-6. A charge transporting layer with a thickness of about 15 μm was formed on the charge generating layer in substantially the same manner as in Example I-6 except that the hydrazone compound No. II-5 was used instead of the compound No. I-5.

The photoconductor thus obtained was charged by corona discharge at -6.0 kV for 0.2 second and examined with respect to electrophotographic characteristics in the same manner as in Example II-5, obtaining good results, namely V_(s) =-630 V and E_(1/2) =6.9 lux·sec.

EXAMPLE II-7

Photoconductors were produced by forming respective photosensitive layers in substantially the same manner as in Example II-4 except that the compounds Nos. II-6 to II-32 were respectively used instead of the compound No. II-4. The results obtained by using the electrostatic recording paper testing apparatus Model SP-428 are shown in Table 4. Table 4 shows the half decay exposure amounts E_(1/2) (lux·sec) obtained under the experimental conditions where the photoconductors were positively charged in the dark by corona discharge at +6.0 kV for 10 seconds and irradiated with white light at an illuminance of 2 luxes.

                  TABLE 4                                                          ______________________________________                                                         E.sub.1/2                                                      Compound No.    (lux · sec)                                           ______________________________________                                         II-6            5.9                                                            II-7            5.8                                                            II-8            6.0                                                            II-9            6.6                                                            II-10           5.9                                                            II-11           6.7                                                            II-12           7.9                                                            II-13           6.8                                                            II-14           6.1                                                            II-15           6.5                                                            II-16           4.8                                                            II-17           5.9                                                            II-18           5.7                                                            II-19           5.1                                                            II-20           6.8                                                            II-21           5.8                                                            II-22           5.4                                                            II-23           6.9                                                            II-24           5.7                                                            II-25           6.1                                                            II-26           6.5                                                            II-27           5.4                                                            II-28           6.8                                                            II-29           5.9                                                            II-30           7.4                                                            II-31           7.3                                                            II-32           6.9                                                            ______________________________________                                    

As can be seen in Table 4, the photoconductors using the respective hydrazone compounds Nos. II-6 to II-32 as a charge transporting substance were satisfactory with respect to the half decay exposure amount E_(1/2).

According to the present invention, when a hydrazone compound represented by any one of the aforementioned chemical formulae is used in a photosensitive layer formed on an electroconductive substrate, as a charge transporting substance, the resulting photoconductor shows a high sensitivity and excellent characteristics in repeated use when adapted to either a positive charge mode or a negative charge mode. A suitable charge generating substance can be chosen so as to be adapted to the kind of exposure light source. By way of example, a phthalocyanine compound or a bisazo compound can be used as a charge generating substance to provide a photoconductor capable of being used in semiconductor laser printers. If necessary, a covering layer may be provided on the surface of the photoconductor to improve the durability thereof.

The invention has been described above in detail with respect to preferred embodiments, and it will now be apparent from the foregoing to those skilled in the art that changes and modifications may be made without departing from the invention in its broader aspects, and it is the invention, therefore, in the appended claims to cover all such changes and modifications other than those specifically described above. 

What is claimed is:
 1. A photoconductor for electrophotography comprising:a substrate; and a photoconductive layer formed on said substrate, said photoconductor layer including a charge generating substance and at least one hydrazone compound represented by the following general formula (I) as a charge transporting substance: ##STR12## wherein each of R₁, R₂, R₃, R₄, R₅, and R₆ stands for a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, a hydroxy group, a nitro group, an allyl group, or an aryl or an amino group, both of which may have at least one substituent; and n stands for an integer of 0, 1 or
 2. 2. A photoconductor as claimed in claim 1, wherein said photoconductive layer comprises a layer including a dispersion of said charge generating substance and a charge transport substance selected from hydrazone compounds represented by the general formulae (I) in a binder resin.
 3. A photoconductor as claimed in claim 1, wherein said photoconductive layer comprises a laminate of a charge transporting layer including a charge transporting substance selected from hydrazone compounds represented by the general formulae (I) and a charge generating layer.
 4. A photoconductor for electrophotography comprising:a substrate; and a photoconductive layer formed on said substrate, said photoconductive layer including a charge generating substance and a least one hydrazone compound represented by the following general formula (II) as a charge transporting substance: ##STR13## wherein each of R₇, R₈, R₉, R₁₀, and R₁₁ stands for a hydrogen atom, a hydroxy group, an alkyl group, an alkoxy group, a hydroxy group, an acyl group, a nitro group, or an aryl group or an amino group, both of which may have at least one substituent, and m stands for an integer 2, 3, 4 or 5; n stands for an integer of 0, 1 or
 2. 5. A photoconductor as claimed in claim 4, wherein said photoconductive layer comprises a layer including a dispersion of said charge generating substance and a charge transporting substance selected from hydrazone compounds represented by the general formulae (II) in a binder resin.
 6. A photoconductor as claimed on claim 4, wherein said photoconductive layer comprises a laminate of a charge transporting layer including a charge transporting substance selected from hydrazone compounds represented by the general formulae (II) and a charge generating layer including said charge generating substance. 